| According to ČSN (Czech Standards) | According to DIN 1691 | Rm/MPa | Note | Structure |
| 422410 | GG-10 | 20 | - | Ferrite - Perlite |
| 422415 | GG-15 | 15 | - | Ferrite - Perlite |
| 422420 | GG-20 | 200 | - | Ferrite - Perlite |
| 422425 | GG-25 | 250 | - | Perlite |
| 422430 | GG-30 | 300 | - | Perlite |
| 422465 | - | 98 | Silicon, heat-resistant | Ferrite - Perlite |
| 422481 | - | 147 | Al, Cr heat-resistant Ferrite | Ferrite - Perlite |
| 422483 | - | 59 | Silicon, ... | - |
| According to EN | Equivalent according to traditional ČSN designation | Equivalent according to traditional DIN 1693 designation | Tensile Strength Rm N/mm2 min. | Yield Strength 0,2% Rp0,2 N/mm2 min. | Elongation A5 % | Structure |
| EN-GJS-350-22-LT | - | GGG 35.3 | 350 | 220 | 22 | ferit |
| EN-GJS-350-22 | 422303 | GGG 35.3 | 350 | 220 | 22 | Ferrite |
| EN-GJS-400-18-LT | 422314 | GGG 40.3 | 400 | 240 | 18 | Ferrite |
| EN-GJS-400-18 | 422314 | GGG 40.3-18 | 400 | 250 | 18 | Ferrite |
| EN-GJS-400-15 | 422304 | GGG 40-15 | 400 | 250 | 15 | Ferrite |
| EN-GJS-450-10 | - | - | 450 | 310 | 10 | Ferrite |
| EN-GJS-500-7 | 422305 | GGG 50 | 500 | 320 | 7 | Perlite-Ferrite |
| EN-GJS-600-3 | 422306 | GGG 60 | 600 | 370 | 3 | Perlite-Ferrite |
| EN-GJS-700-2 | 422307 | GGG 70 | 700 | 420 | 2 | Perlite-Ferrite |
| EN-GJS-800-2 | 422308 | GGG 80 | 800 | 480 | 2 | Perlite |
| 422340 | - | 300 | - | - | Perlite | |
| 422484 | - | 196 | Alloyed Al, heat-resistant up to 1150°C | - | Ferrite |
Cast irons with a basic structure composed of austenite. These are highly alloyed cast irons designed for use in extreme conditions unsuitable for other types of materials. Each type of these cast irons guarantees specific properties such as corrosion resistance in aggressive environments, heat resistance, fire resistance, abrasion resistance, non-magnetism, sliding properties, etc.
| According to DIN 1694 | According to ASTM A436 | Rm/Mpa | Rp0,2/Mpa | A5(%) | HB | Graphite Shape |
| GGG NiCr 20-2 | D-2B | 380 | 210 | 8 | 140-200 | Nodular |
| GGG NiCr 20-3 | D-2B | 400 | 220 | 6 | 150-255 | Nodular |
| GGG NiSiCr 20-4-2 | - | 370 | 220 | 10 | 180-230 | Nodular |
| GGG Ni 22 | D-2C | 380 | 210 | 20 | 130-170 | Nodular |
| GGG NiMn 23-4 | D-2M | 420 | 180 | 27 | 150-180 | Nodular |
| GGG NiCr 30-3 | D-3 | 380 | 220 | 7 | 140-200 | Nodular |
| GGG NiCr 30-1 | D-3A | 380 | 210 | 13 | 130-190 | Nodular |
| GGG NiSiCr 30-5-5 | D-4 | 400 | 240 | 1 | 170-250 | Nodular |
| GGG Ni 35 | D-5 | 380 | 210 | 20 | 130-180 | Nodular |
| GGG NiCr 35-3 | D-55 | 380 | 220 | 5 | 140-190 | Nodular |
| GGG NiMn 13-7 | - | 400 | 220 | 10 | 120-150 | Nodular |
| GG NiCuCr 1562 | - | 170 | - | 1 | 140-200 | Nodular |
| Properties of wear-resistant cast iron | |
| Hardness | 550 - 700 HB |
| Bending strength | 620 - 750 MPa |
| Quarry | white |
| Machinability | very bad |